Chain scission and branching in irradiated poly(tetrafluoroethylene-co-hexafluoropropylene)
|
Date
|
31.12.2003
|
Number
|
11599
|
Abstract
|
The radiation chemistry of poly(tetrafluoroethylene-<I>co</I>-hexafluoropropylene) (FEP) with a TFE mole fraction of 0.90 has been studied under vacuum using <SUP>60</SUP>Co <IMGSRC="/giflibrary/12/gamma.gif"BORDER="0">-radiation over a range of temperatures and absorbed doses. The radiolysis temperatures were 300, 363, 423, 523 and 543 K. New structure formation in the copolymers was analysed by solid-state <SUP>19</SUP>F NMR spectroscopy. The new structures formed in the copolymers have been identified and the <I>G</I>-values for the formation of new chemical structures have been investigated at 363 and 523 K. These two temperatures are just above and just below the polymer <I>T</I><SUB>g</SUB> and <I>T</I><SUB>m</SUB>, respectively. At the lower temperature, there was no evidence for any chain branching and an estimate of <I>G</I>(S) of 1.0 was obtained. A value of <I>G</I>(S) of 1.3 and a minimum value of <I>G</I>(X)<SUB>Y</SUB> of 1.3 were obtained at 523 K. Copyright © 2003 Society of Chemical Industry
|
Publisher
|
Polymer International
|
Wikidata
|
|
Citation
|
Polymer International 52 (2003) 1725-1733
|
DOI
|
https://doi.org/10.1002/pi.1299
|
Tags
|
|