Title In-situ imidization analysis in microscale thin films of an ester-type photosensitive polyimide for microelectronic packaging applications
Date 01.11.2016
Number 51448
Abstract The imidization reaction in thin films of an ester-type photosensitive polyimide is investigated in the temperature range of 50–450 °C by temperature dependent rapid-scan in-situ FT-IR spectroscopy, thermo-ellipsometric analysis and thermogravimetric analysis coupled with evolved gas analysis. The influence of the UV crosslinkable methacrylic functional group in the polymer sidechain on the imidization reaction is studied. For non-crosslinked precursor films the imidization is completed at ˜250 °C. Depending on the amount of crosslinking the temperature to achieve full imidization is shifted to higher values. Above a certain amount of crosslinking the degree of imidization is limited to ˜95% for temperatures below 280 °C. The reaction continues by further increase of the temperature to >340 °C. Evolved gas analyses indicate that the cleave-out of crosslinker is required to finish the imidization. The film shrinkage and weight loss is correlated to the degree of imidization.
Publisher European Polymer Journal
Identifier 0
Citation European Polymer Journal 84 (2016) 279-291
Authors Windrich, F. ; Kappert, E. J. ; Malanin, M. ; Eichhorn, K.-J. ; Häußler, L. ; Benes, N. E. ; Voit, B.
Tags photosensitive polyimide in-situ ellipsometry thermal imidization low-temperature cure

Back to list