Title Nucleation efficiency of fillers in polymer crystallization studied by fast scanning calorimetry: Carbon nanotubes in polypropylene
Date 05.05.2017
Number 52963
Abstract The influence of multi-walled carbon nanotubes (0–5 wt%) on the crystallization process in isotactic polypropylene has been investigated by DSC and fast scanning calorimetry. In the non-isothermal experiments the crystallization temperature shifts to higher temperatures with increasing nanotube content, aCNT, whereas the polymer crystallinity was not significantly influenced. The critical cooling rate, ßc, at which the PP does not crystallize, increases with increasing of aCNT. From ßc and aCNT a nucleation efficiency parameter was derived, which is independent of crystallization temperature and filler content. Isothermal crystallization experiments allow differentiating between a-phase and mesophase crystallization. Nanotubes accelerate only the a-phase formation. To describe the efficiency of a nucleation agent an acceleration factor, e, was introduced, which is the ratio of the characteristic crystallization time of unfilled and filled polymer. For the a-phase formation the acceleration factor e is related to the number of nuclei per nanotube and the specific effect of the filler on the growth rate.
URL https://doi.org/10.1016/j.polymer.2017.03.072
Publisher Polymer
Identifier 0
Citation Polymer 116 (2017) 160-172
DOI https://doi.org/10.1016/j.polymer.2017.03.072
Authors Schawe, J.E.K. ; Pötschke, P. ; Alig, I.
Tags

Back to list