Authors Kasbi, S.F. ; Jafari, S.H. ; Khonakdar, H. A. ; Goodarzi, V. ; Torabi, A.
Title beta-Polymorph enhancement in poly(vinylidene fluoride) by blending with polyamide 6 and barium titanate nanoparticles
Date 07.07.2020
Number 58683
Abstract Polyamide 6 (PA6) as a cost–effective polar polymer and barium titanate (BT) as piezoelectric ceramic nanofiller were melt compounded with poly(vinylidene fluoride) (PVDF) matrix to enhance the ß electroactive phase. A series of samples with two blending ratios of PVDF/PA6 (90/10 and 70/30 [wt%/wt%]) each containing 1, 3, and 5 wt% of BT were prepared. The SEM results revealed that the addition of BT to the neat blends refined the biphasic morphology which is mainly due to selective localization of BTs in PA6 dispersed phase as confirmed by TEM observation and wetting parameter predictions. The EDX analysis demonstrated a uniform distribution of BT nanoparticles in the filled systems. FTIR and XRD results showed that ß content increased as a result of blending while the a phase was suppressed. The BT nanoparticles inclusion to the blends showed a synergistic effect on the ß–polymorph content. These results in combination with the data derived from DSC (indicating reduction of the total crystallinity) complement the idea of ß enhancement by the addition of BT nanoparticles and PA6 into PVDF.
Publisher Journal of Applied Polymer Science
Wikidata
Citation Journal of Applied Polymer Science 137 (2020) Article Number: e49403
DOI https://doi.org/10.1002/APP.49403