Title Influence of precursor film microstructure on properties of HDPE microporous membranes prepared by stretching
Date 20.04.2017
Number 52461
Abstract Oriented HDPE films having a stacked lamellar morphology were prepared to develop microporous membranes through cast film extrusion followed by stretching. Applying higher draw ratios (DR) and annealing the cast films improved crystal alignments remarkably. It was shown the improvement in c-axis orientation upon annealing was more significant for the films prepared with lower DR. Furthermore, applying Raman spectroscopy, the amorphous mass fraction of the films was obtained. Subsequently, considering a three-phase structure (i.e., crystal, amorphous and interphase), the interphase content of the films was also determined. A distinct DR dependence of the interphase content was noticed. It was observed that in addition to crystal perfection upon annealing, the amorphous phase fraction was also decreased due to possibly increase in free volume, promoting lamellar separation and cavitation during the subsequent stretching step. SEM images of the membranes surfaces as well as their normalized water vapor transmission rate (WVTR) values indicated a more uniform pore formation and increased permeability with DR. Furthermore, it was found that lower interphase content in the films with higher DR favors lamellar separation. However, permeability in the stretched precursor films with DR higher than a certain level (DR·=·93) was not improved significantly. Moreover, crystallinity and crystal orientation of produced membranes were investigated. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 44725.
URL http://dx.doi.org/10.1002/app.44725
Publisher Journal of Applied Polymer Science
Identifier 0
Citation Journal of Applied Polymer Science 134 (2017) Art.No. 44725
DOI http://dx.doi.org/10.1002/app.44725
Authors Yadegari, A. ; Morshedian, J. ; Khonakdar, H. A. ; Wagenknecht, U. ; Heinrich, G.
Tags

Back to list