Authors
|
Zhandarov, S. ; Pisanova, E. ; Mäder, E.
|
Title
|
Is there any contradiction between the stress and energy failure criteria in micromechanical tests? Pt. II. Crack propagation: Effect of friction on force-displacement curves
|
Date
|
08.11.2000
|
Number
|
9556
|
Abstract
|
In micromechanical tests for estimating fiber-matrix interfacial properties, such as the pull-out and microbond tests, fiber debonding from a matrix is often accompanied by friction in debonded areas. In the present study, force-displacement curves, which are usually recorded in these tests, were modeled with taking interfacial friction into consideration. The friction stress was assumed, as a first approximation, to be constant across the interface. Two different approaches to interfacial failure were used: the shear-lag approach with a stress-based debonding criterion (the ultimate interfacial shear strength) and the linear elastic fracture mechanics approach using the critical energy release rate as a condition for crack propagation. The force-displacement curves derived from both models are in good agreement with each other and with experimental micromechanical data. It was shown that any pull-out and microbond experiment comprises four stages: (1) linear loading up to the point where debonding starts; (2) stable crack propagation with friction-controlled debonding; (3) catastrophic debonding; and (4) post-debonding friction. Stable crack propagation was shown to be controlled by both friction and release of residual thermal stresses. An algorithm for estimating both fiber-matrix adhesion and interfacial friction from the microbond and pull-out tests data has been proposed.
|
Publisher
|
Composite Interfaces
|
Wikidata
|
|
Citation
|
Composite Interfaces 7 (2000) 149-175
|
DOI
|
https://doi.org/10.1163/156855400300185289
|
Tags
|
|